Chemical composition for 410S stainelss steel
|
Grade |
C(%) |
Si(%) |
Mn(%) |
P(%) |
S(%) |
Cr(%) |
Ni(%) |
|
410S |
≤0.08 |
≤1.0 |
≤1.0 |
≤0.04 |
≤0.03 |
11.5-13.5 |
≤0.6 |
Mechanical property for 410S stainless steel
|
Grade |
tensile strength Mpa |
Yield Strength Mpa |
Elongation (%) |
rate of reduction in area (%) |
Density (g/cm3) |
|
410S |
≥490 |
≥345 |
≥24 |
≥60 |
7.75 |
Specifications for 410S stainless steel
|
Technical |
Thickness |
Width |
finish |
Origin |
|
Cold rolled |
0.3mm-5.0mm |
Standard width in China:1000mm 1219mm Special width:can be ordered |
2B / BA / No/4 / HL / Mirror etc |
TISCO / Baosteel etc |
Applications for 410S stainless steel
410S is to improve the corrosion resistance of the steel and formability of steel, mainly used in the manufacture of water vapor, ammonium bicarbonate solution, parts and equipment of the oil sulfur corrosion heat lining etc..
Standards for 410S stainless steel
GB: 06Cr13 (Standards from China)
ASTM: 410S (Standards from USA)
DIN: 1.4000 (Standards from Europe)
JIS: SUS410S (Standards from Japan)
The weight calculation method for 410S stainless steel
Weight(KG/PC)=thickness(mm) x width(Meter) x length(Meter) x 7.75
- *
- *